Adhesives/Sealants - Aerospace/Defense
Product
Cure System
Rheology
Durometer
Work Time
Data Sheet
Comment
Platinum
For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.
Platinum
Flowable / Self Leveling
50 Type A
3 hours
*4 )Primed Lap Shear 225 psi (1.6 MPa), Optically Clear
Platinum
Flowable / Self Leveling
40 Type A
3 hours
Fast Cure, Low Density*,4 )Primed Lap Shear 175 psi (1.2 MPa)
Platinum
Flowable / Self Leveling
30 Type A
4 hours
White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.
Platinum
Flowable / Self Leveling
30 Type A
3.5 hours
Low / High Temperature, Flowable, Fast Cure
Platinum
Thixotropic / non-slump
30 Type A
3.5 hours
50% M fluoro. Black and will RTV in 48 hrs
Platinum
Flowable / Self Leveling
30 Type A
N/A
White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.
Platinum
Flowable / Self Leveling
15 Type A
15 hours
Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.
Oxime
Flowable / Self Leveling
40 Type A
Recommended for extended operation at elevated temperatures.