| Product | Cure
System | Cure
Time / C° | Duro. | Tensile | Elong. | Tear | Rheology | Spec. Gravity | MSDS | Comments |
|
CAT-01
| Non-curing | | | | | |
| |
| Polymerization Catalyst |
|
CAT-02
| Non-curing | | | | | |
| |
| Polymerization catalyst |
|
CAT-07
| Non-Curing | | | | | |
680 cP
| |
| Polymerization Catalyst |
|
MED-1000
| Acetoxy | 72 h / R.T., H. | 25 | 1300 | 775 | 75 |
| 1.08 |
| Self-Leveling |
|
R-1001
| | | | | | |
| |
| VM&P Naphtha |
|
R-1002
| | | | | | |
3 cSt
| 0.95 |
| Dimethly Cyclic |
|
R-1005
| Non-Curing | | | | | |
| |
| 99.5% D4 Content |
|
R-1007
| Oxime | 7 D / 25 | 30 | | | |
| 1.52 |
| Thermal control Coating / Marking Ink |
|
R-1008
| | 7 d / R.T, H. | | | | |
1.2k
| |
| Available in translucent, white, black, red, orange, yellow, green, blue, violet |
|
R-1009
| Oxime | 7 D / R.T. | 45 | 1150 | 650 | 95 |
6.2k cP
| 1.10 |
| RTV Dispersion Coating / Conformal, 32% Solids |
|
MED-1011
| Acetoxy | < 10 m | 25 | 1400 | 750 | 100 |
100 g/min
| 1.12 |
| Flowable |
|
CAT-102
| Non-curing | | | | | |
| |
| Peroxide catalyst masterbatch |
|
XL-103
| Non-Curing | | | | | |
200 cP
| 0.97 |
| Methylhydrogen dimethylsiloxane Low H |
|
MED-1031
| Oxime | 7 D / R.T. | 35 | 1075 | 400 | 80 |
0.5
| 1.11 |
| No Acidic Leaving Group |
|
MED-1037
| Acetoxy | 3 D / R.T. | 25 | 625 | 550 | |
0.75
| 1.07 |
| Non-Slump, Thixotropic |
|
MED-1055
| Acetoxy | 72 H, R.T. | 35 | 820 | 400% | 50 |
| 1.35 |
| Solvent resistant |
|
R3-1075
| Oxime | 7 D / R.T. | 40 | 700 | 350 | 40 |
3.3k cP
| 1.06 |
| RTV Dispersion Coating / Conformal, 60% Solids |
|
R-1082
| Acetoxy | 5 D / R.T., H | 25 | 1425 | 950 | 125 |
700
| 1.09 |
| Ice Phobic; One-Part, 20% Solids |
|
XL-110
| Non-Curing | | | | | |
4 cP
| 0.97 |
| Methylhydrogen dimethylsiloxane High H |
|
XL-112
| Non-Curing | | | | | |
40 cP
| 0.97 |
| Methylhydrogen dimethylsiloxane Medium H |
|
R-1130
| Oxime | 7 D / R.T. | 35 | 850 | 325 | 40 |
0.5
| 1.10 |
| RTV Adhesive |
|
MED-1131
| Oxime | 7 D / R.T. | 35 | 1075 | 400 | 80 |
0.5
| 1.11 |
| No Acidic Leaving Group |
|
MED-1137
| Acetoxy | 3 D / R.T. | 25 | 625 | 550 | |
0.75
| 1.07 |
| Non-Slump, Thixotropic |
|
MED12-1137
| Acetoxy | 72 H / R.T. | 25 | 650 | 525 | |
1
| 1.18 |
| White adhesive |
|
R-1140
| Acetoxy | 7 D / R.T. | 30 | 600 | 350 | 40 |
| 1.08 |
| RTV Adhesive |
|
R2-1140
| Acetoxy | 7 D / R.T. | 25 | 200 | 325 | 20 |
| 1.03 |
| RTV Adhesive |
|
R4-1140
| Acetoxy | 3 D / R. T. | 25 | 1400 | 750 | 100 |
2
| 1.12 |
| RTV Adhesive |
|
CV-1142
| Oxime | 7 d / R.T., H | 45 | 700 | 300 | |
| 1.11 |
| Great for Spot Bonding, Available in Black & White |
|
CV1-1142
| Oxime | 7 D / R.T. | 30 | 400 | 200 | |
13k
| |
| Self-leveling, Available in Black & White |
|
CV1-1142
| Oxime | 7 D / R.T. | 30 | 400 | 200 | |
60
| |
| Self-leveling, Available in Black & White
NGC Specification C600080 |
|
CV2-1142
| Oxime | 7 d / R.T., H | 50 | | | |
| |
| Non-Slump, Available in Black & White |
|
CV3-1142
| Oxime | 7 d / R.T., H | 45 | 675 | 300 | |
| 1.11 |
| Great for Spot Bonding, Available in Black & White |
|
CV9-1142
| Oxime | 7 d / R.T., H | 55 | 400 | 85 | |
| 0.82 |
| High Durometer, Low Density |
|
CV7-1142-1
| Oxime | 7 d / R.T., H | 40 | 700 | 300 | 60 |
| 1.13 |
| Non-Slump, Non-Corrosive |
|
CV1-1142-4
| Oxime | 7 D / R.T. | 35 | 400 | 200 | |
60
| 1.05 |
| Self-leveling, Built-in UV Tracer
NGC Specification C600080 |
|
CV1-1142-4
| Oxime | 7 D / R.T., H | 35 | 350 | 200 | |
60
| |
| Self-leveling, Built-in UV Tracer |
|
CV-1143
| Oxime | 7 d / R.T., H | 45 | 800 | 400 | |
| 1.10 |
| Non-Slump, Non-Corrosive |
|
CV-1144-0
| Oxime | 7 d / R.T., H | | | | |
240 cP
| 1.00 |
| 60% Solids, Atomic Oxygen Protective Overcoat |
|
CV1-1144-0
| Oxime | 7 d / R.T., H | | | | |
850 cP
| 1.11 |
| 50% Solids |
|
CV3-1144-1
| Oxime | 7 d / R.T., H | | | | |
900 cP
| |
| 60% Solids, White Overcoat |
|
CV-1146-2
| Oxime | 7 d / R.T., H | | | | |
2.4k cP
| 1.26 |
| 72% Solids, Black |
|
CV2-1147
| Oxime | 7 d / R.T., H | | | | |
2k cP
| 1.12 |
| 60% Solids, Non-blocking Overcoat |
|
CV-1148
| Oxime | 7 d / R.T., H | | | | |
7.5k
| 1.34 |
| 70% Solids |
|
CV1-1148
| Oxime | 7 D / R.T. | | | | |
6k cP
| 1.06 |
| 40% Solids
NGC Specification C843757 |
|
CV1-1148
| Oxime | 7 d / R.T., H | | | | |
5k cP
| 1.07 |
| 40% Solids |
|
CV2-1148
| Oxime | 7 d / R.T., H | | | | |
| 1.07 |
| Non-Slump, Black |
|
CV-1152
| Oxime | 7 d / R.T., H | | | | |
7.3k cP
| 1.01 |
| 100% Solids, Protective Overcoat |
|
CV-1161
| | 2 h / 60 | | | | |
3k
| |
| 50% Solids, 7.5 ppi Release Force |
|
CV2-1161
| Peroxide | 20 m / 60 then 20 m / 175 | | | | |
770
| |
| 35% Solids, 2.5ppi Release Force |
|
CV3-1161
| | | | | | |
1.2k
| |
| Pressure Sensitive Silicone Adhesive |
|
CV4-1161-5
| | | | | | |
| |
| 0.005 inches (5 microns) Double Side Tape, Kapton® Center, 2.5 ppi |
|
CV4-1161-5
| | | | | | |
| |
| 0.005 inches (5 microns) Double Side Tape, Kapton® Center, 2.0 ppi
NGC Specification C878374 |
|
R-1182
| | | | | | |
| |
| Provides a RTV, low-friction coating
on cured silicone substrates |
|
SP-120
| Non-curing | | | | | |
1 cP
| 0.77 |
| General Purpose |
|
SP-121
| Non-Curing | | | | | |
1 cP
| 0.76 |
| General Purpose Primer |
|
SP-121
| Non-curing | | | | | |
1 cP
| 0.78 |
| General Purpose Primer
NGC Specification QFM-0433 |
|
SP-124
| Non-curing | | | | | |
1 cP
| 0.79 |
| Condensation Cure Systems, 9% Solids |
|
LS-1246
| Non-curing | | | | | |
| |
| Thixotropic optical silicone grease |
|
LS-1249
| | Non-curing | | | | |
| 1.10 |
| Thixotropic optical silicone grease |
|
XL-128
| Non-Curing | | | | | |
| |
| Inhibitor, Methyl Butynol |
|
SP-133
| | Non-curing | | | | |
1.5 cSt
| 0.81 |
| Polyimide Film Adhesion |
|
CF1-135
| Hydrolysis | 30 Min R.T., 50% H | | | | |
| |
| Addition cure systems |
|
CF2-135
| Non-Curing | | | | | |
1 cP
| |
| Addition Cure Systems, 4.6% Solids
NGC Specification 960119 |
|
CF2-135
| Non-Curing | | | | | |
1 cP
| 0.77 |
| Addition Cure Systems, 4.5% Solids |
|
CF6-135
| Hydrolysis | 30 Min, R.T., 50% H. | | | | |
| .78 |
| Addition cure system |
|
SP-135
| Non-Curing | | | | | |
1 cP
| 0.77 |
| Addition cure system |
|
MED-1356
| Non-Curing | 90 M / 150 | | | | |
1.4k cP
| |
| PSA / Ethyl Acetate |
|
CF1-136
| Hydrolysis | 30 Min. R.T., 50% H | | | | |
| |
| Addition cure systems |
|
CF6-136
| Hydrolysis | 30 Min, R.T., 50% H. | | | | |
| .78 |
| Addition cure system |
|
SP-136
| Non-curing | | | | | |
| 0.77 |
| Addition cure system |
|
CF2-137
| Non-Curing | | | | | |
| 0.77 |
| Addition Cure, UV Tracer |
|
DDR-1370
| see product profile | | | | | |
1.4k
| |
| cohesive PSA dispersed in solvent |
|
R-1400
| Platinum | 1 H / 150 | 19 | 825 | 750 | 110 |
400k cP
| 1.18 |
| Low durometer, Non Flowable, One-Part Elastomer |
|
CF1-141
| Non-Curing | | | | | |
1 cP
| 0.80 |
| Addition Cure, IPA Solvent |
|
SP-142
| Non-curing | | | | | |
1 cP
| 0.79 |
| Polycarbonate Adhesion |
|
SP-144
| Non-curing | | | | | |
| 0.87 |
| Addition cure systems |
|
SP-145
| Non-curing | | | | | |
1.05 cP
| 1.06 |
| Improves adhesion to various substrates |
|
SP-145-3
| Non-curing | | | | | |
1.05 cP
| 1.06 |
| Improves adhesion to various substrates |
|
XL-150
| Non-Curing | | | | | |
11 cP
| 0.97 |
| Methylhydrogen Fluorosiloxane High H |
|
CV-1500
| Oxime | 7 D / R.T. | 75 | 675 | 20 | |
0
| 1.25 |
| 3.5 ohm-cm, 0.32 W/mK, Primed Lap Shear 350psi (2.4 Mpa)
NGC Specification C816529 |
|
CV-1500
| Oxime | 7 d / R.T., H | 80 | 650 | 20 | |
| 1.25 |
| 3.5 ohm-cm, Primed Lap Shear 325psi (2.2 Mpa) |
|
R-1505
| Oxime | 7 D / R.T. | 75 | 550 | 20 | |
| 1.24 |
| Static Dissipation, 30 ohm-cm |
|
MED-1511
| Acetoxy | 72 h / R.T. | 25 | 1400 | 750 | 100 |
| 1.12 |
| Flowable |
|
MED-1555
| Acetoxy | 72 H / R.T. | 35 | 820 | 400 | 50 |
| 35 |
| Solvent resistant |
|
MED-160
| Non-curing | | | | | |
1 cP
| 0.77 |
| General Purpose Primer |
|
R-1600
| Oxime | 7 D / R.T. | 45 | 650 | 300 | 60 |
| 1.10 |
| Low/High Temperature, RTV |
|
MED1-161
| Non-curing | | | | | |
1 cP
| 0.77 |
| Primer for Platinum-cured Systems |
|
MED2-161
| Non-curing | | | | | |
1
| 0.77 |
| Designed for use with platinum cure systems |
|
MED6-161
| Non-curing | | | | | |
1
| 0.78 |
| Primer for platimum-cure systems |
|
MED-162
| Hydrolysis | 30 M / R.T., 50% H. | | | | |
1 cP
| 0.79 |
| Primer for Platinum Systems |
|
MED-163
| Hydrolysis | 30 M / R.T., 50% H. | | | | |
1 cP
| 0.80 |
| Primer for Platinum Systems |
|
MED-164
| Hydrolysis | 30 Min R.T., 50% H. | | | | |
1 cP
| 0.79 |
| Designed for use with condensation cure silicones |
|
MED-165
| Non-curing | | | | | |
1
| 0.77 |
| Designed for use with platinum-cured systems |
|
MED-166
| Non-Curing | | | | | |
2.0 cP
| .80 |
| Designed for use with platinum-cured systems |
|
MED-2000
| Acetoxy | 72 h / R.T. | 25 | 1300 | 775 | 75 |
| 1.08 |
| Self-Leveling |
|
MED-2014
| Platinum | 1* | 35 | 1800 | 800 | 185 |
3.4k cP
| 1.10 |
| One Part, in Xylene |
|
SP1-204
| Non-Curing | | | | | |
| .79 |
| 1 & 2 Part RTV System. 3.3 % S. |
|
MED-2045
| Platinum | 10 M / 171 | 40 | 1525 | 800 | 200 |
95
| |
| 3-Part |
|
R-2100-2
| Addition | 5 m / 150°C | | | | |
A:800/B:2.8k
| |
| Black ink, various applications |
|
R-2100-7
| Addition | 5 m / 150°C | | | | |
A:2.1k/B:850
| 0 |
| Blue ink, various applications |
|
R-2140
| Platinum | 5 m / 177°C | 40 | 850 | 320 | 150 |
A:12k/B:270
| 1.09 |
| Adhesive, encapsulating compound or mold-making material |
|
R-2145
| Platinum | 2 H / 65 | 45 | 1050 | 400 | 150 |
280
| 1.17 |
| Extremely Tough, Fast Cure Elastomer |
|
R1-2145
| Platinum | 2 H / 65 | 45 | 1000 | 400 | 150 |
270
| 1.18 |
| Modulus 300psi (2.1 Mpa) |
|
R1-2145
| Platinum | 2 h / 65 | 45 | 1000 | 400 | 190 |
| 1.16 |
| Adhesive for bonding and
sealing silicones to each
other and other substrates
such as metals and plastics |
|
R-2160
| Platinum | 30 M / 150 | 20 | 750 | 625 | 150 |
A:250k/B:650 cP
| 1.20 |
| High Temperature Elastomer |
|
R3-2160
| | 15 m / 150 | 35 | 550 | 525 | 130 |
| 1.18 |
| High temp adhesive/sealant, primed lap shear 200 psi |
|
MED-2174
| Peroxide | 5 M / 116 | 50 | 1200 | 775 | 225 |
105
| 1.15 |
| Peroxide |
|
R-2180
| Platinum | > 30 m R.T., H | 40 | 1700 | 1050 | 300 |
3.1k cP
| |
| Ice Phobic; Tough silicone dispersion |
|
R-2180-2
| Platinum | See Comments | 45 | 1650 | 1000 | 300 |
3.3k
| |
| Ice Phobic; Cure: 30 M / 25 °C : 45 M / 75 °C : 135 M / 150 °C, 20% Solids |
|
R-2182
| | 5 m / 150 | | | | |
| 0.96 |
| Low coefficient of friction silicone coating |
|
R-2183
| | ramp cure | 35 | 1550 | 800 | 175 |
850 cP
| |
| For dip casting and heat-curing of thin elastomeric films |
|
CF13-2186
| Platinum | 15 M / 150 | 20 | 550 | 500 | |
| 1.07 |
| Low Viscosity, Fast Cure |
|
CF15-2186
| Platinum | 1 D / R.T. | 25 | 1200 | 625 | 100 |
A:80k/B:50k
| A:1.12/B:1.11 |
| Short Work Time, Fast Cure Elastomer |
|
CF16-2186
| Platinum | 60 M / 100 | 30 | 1175 | 550 | 80 |
70k cP
| 1.10 |
| Medium Work Time, Fast Cure Elastomer |
|
CF18-2186
| Platinum | 15 M / 150 | 17 | 650 | 575 | |
A:23k/B:18k
| |
| Non-corrosive |
|
CF19-2186
| Platinum | 30 M / 150 | 25 | 1100 | 600 | 80 |
A:85k/B:65k cP
| 1.11 |
| Longer Work Time, Soft Duro |
|
CF2-2186
| Platinum | 10 M / 150 | 20 | 800 | 600 | 90 |
| 1.10 |
| Medium Viscosity |
|
CF20-2186
| Platinum | 60 M / 100 | 30 | 1100 | 600 | 80 |
A:80k/B:50k
| 1.10 |
| Longer Work Time |
|
R-2186
| Platinum | 15 M / 150 | 30 | 1100 | 500 | 80 |
| 1.12 |
| All Purpose High Tear Elastomer |
|
R28-2186
| Platinum | 30 m / 150C | 25 | 1150 | 650 | 75 |
| 1.12 |
| Non slumping, easy application |
|
R31-2186
| Platinum | 1 D / R.T. | 20 | 1000 | 775 | 125 |
82k cP
| 1.12 |
| Flowable, Fast Cure Adhesive |
|
R32-2186
| Platinum | 15 M / 150 | 15 | 975 | 850 | 125 |
80k cP
| 1.12 |
| Flowable, Longer Work time, Fast Cure Adhesive |
|
R33-2186
| Platinum | 24 h / R.T., h | 20 | 1,000 | 725 | 150 |
83.5k cP
| 1.12 |
| Flowable, Longer Work Time, Adhesive |
|
R34-2186
| Platinum | 15 M / 120 | Type A 48 | 830 | 340 | |
| 1.09 |
| Adhesive for bonding and sealing silicones |
|
R-2186-2
| Platinum | 15 M / 150 | 35 | 1050 | 500 | 100 |
| 1.15 |
| All Purpose High Tear Elastomer-Black |
|
CV-2187
| Platinum | 15 m / 150 | 35 | 925 | 400 | 75 |
90k cP
| 1.10 |
| Tough, Flowable, Fast Cure Elastomer |
|
R-2187
| Platinum | 2 HR / 70 | Type A 42 | 790 | 175 | 50 ppi |
23k cP
| 1.12 |
| Enhanced performance in extreme temperatures |
|
R-2188
| Platinum | 30 m / 150 | 20 | 475 | 350 | |
A:13.5k/B:9k cP
| 1.05 |
| Low Viscosity, Low Modulus Elastomer |
|
CV-2189-2
| Platinum | 15 m / 200 | 17 | 750 | 700 | 50 |
225k
| 1.15 |
| Non-Flowable |
|
R-2200-11
| Platinum | 30 / 150 | 60 | 800 | 135 | 100 |
A:140k/B:3k
| 1.24 |
| Casting, Creating Molds |
|
R-2200-6
| Platinum | 30 m / 150 | 65 | 850 | 90 | 95 |
A:135k/B:3.8k
| 1.23 |
| Casting, Creating Molds |
|
MED-2214
| Platinum | 1* | 35 | 1800 | 800 | 185 |
3.4k cP
| 1.10 |
| One Part, in Xylene |
|
MED-2245
| Platinum | 10 M / 171 | 40 | 1525 | 800 | 200 |
95
| |
| 3-Part |
|
CV-2287
| Platinum | 30 m / 150 | 30 | 725 | 400 | 55 |
85k cP
| 1.11 |
| Low/High Temperature, Flowable, Fast Cure Elastomer |
|
CV-2289
| Platinum | 15 m / 150 | 30 | 750 | 350 | |
| |
| Tough, High Temperature Resistant Elastomer |
|
CV-2289-1
| Platinum | 15 m / 150 | 30 | 700 | 350 | |
A:60k/B:40k cP
| |
| Tack-Free 4 Hrs Max, Work Time 30 Min, Pourable Elastomer |
|
CV1-2289-1
| Platinum | 15 m / 150 | 25 | 650 | 325 | 35 |
A:65k/B:40k cP
| 1.10 |
| Primed Lap Shear 400 psi (2.8 Mpa) |
|
CV2-2289-1
| Platinum | 4 h / 65 | 30 | 450 | 250 | |
A:14k/B:10.5k cP
| |
| Low Viscosity, Primed Lap Shear 300 psi (2.47 Mpa) |
|
CV3-2289-1
| Platinum | 7 d / R.T. | 35 | 175 | 125 | |
A:15k/B:14k cP
| |
| Low Viscosity, Added Micro Balloons for Bond Line Control |
|
CV3-2289-1
| Platinum | 7 D / R.T. | 30 | 175 | 125 | |
A:15k/B:14k cP
| |
| Low Viscosity, Added Micro Balloons for Bond Line Control
NGC Specification 960473 |
|
CV4-2289-1
| Platinum | 30 m / 150 | 30 | 650 | 400 | |
A:1300k/B:1000k cP
| |
| Low modulus |
|
CV7-2289-1
| Platinum | 15 m / 150 | 30 | 700 | 375 | |
A:57.5k/B:400k cP
| |
| Primed Lap Shear 350 psi (2.4 Mpa) |
|
CV-2289-2
| Platinum | 15 m / 150 | 30 | 750 | 400 | 50 |
A:65k/B:40k cP
| |
| Pourable elastomer |
|
R-2350
| Platinum | 45 M / 100 | | | | |
A:28k/B:13k cP
| 0.35 |
| Flame Resistant, 22 lbs/ft3 (0.35 g/cm3) |
|
SFM5-2350
| Platinum | 2 H / R.T. | | | | |
A:55k/B:45k cP
| 0.35 |
| Flame Resistant, 25 lbs/ft3 (0.40 g/cm3) |
|
R1-2354
| Platinum | 10 M / R.T. | | 100 | | |
A:270k/B:260k cP
| 0.45 |
| High Strength/Soft, 40 lbs/ft3 (0.64 g/cm3) |
|
R-2356
| Platinum | 45 M / 100 | | | | |
A:4.1k/B:5.3k cP
| 0.35 |
| Flame Resistant, 28 lbs/ft3 (0.44 g/cm3) |
|
R-2356
| Platinum | 45 M / 100 | | | | |
A:4.1k/B:5.3k cP
| 0.35 |
| Flame Resistant, 28 lbs/ft3 (0.44 g/cm3)
NGC Specification QFM-0061 |
|
R-2370
| Tin Condensation | 10 M / R.T. | | | | |
4.7k cP
| |
| Low Density/Soft, 10 lbs/ft3 (0.16 g/cm3) |
|
R-2380
| Tin Condensation | 10 M / R.T. | | | | |
3.6k cP
| |
| Low Density/Soft, 18 lbs/ft3 (0.30 g/cm3) |
|
CV-2391
| Platinum | 60 m / R.T., H | | | | |
3k
| |
| Low medium density foam, 14lb/ft3 (0.224 g/mL) |
|
EPM-2401
| Non-Curing | | | | | |
| 2.30 |
| Thermally conductive, white silicone grease 0.49 W/mK |
|
EPM-2410
| Platinum | 15 M / 150 | 30 | 675 | 350 | |
A:62k/B:40k cP
| |
| Ideal for Static Mix and Dispense Applications |
|
EPM-2410-1
| Platinum | 15 M / 150 | 30 | 700 | 350 | |
A:60k/B:40k cP
| |
| White |
|
EPM-2410-2
| Platinum | 15 M / 150 | 30 | 800 | 400 | |
A:65k/B:40k cP
| |
| Black |
|
EPM-2411-2
| Platinum | 15 M / 200 | 17 | 750 | 700 | 55 |
300k cP
| 1.16 |
| Shear Thinning Index 2.5 |
|
EPM-2420
| Platinum | 60 M / 65 | 28 | 400 | 150 | |
2.6k cP
| 1.01 |
| Primerless Adhesion |
|
EPM-2421
| Platinum | 15 M / 150 | 50 | 850 | 90 | |
A:3.7k/B:2.6k cP
| |
| Two-part, optically clear silicone |
|
EPM-2422
| Platinum | 4 H / 65 | 40 | 625 | 125 | |
3.5k cP
| 1.04 |
| 1.43 Refractive Index, Low/high Temperature, Primed Lap Shear 160 psi (1.1 Mpa) |
|
EMP-2423
| Platinum | 15 m / 150 | 50 | 1,000 | 125 | |
8k cP
| 1.02 |
| For electronic applications requiring low volatility to avoid condensation in sensitive devices |
|
EPM-2423
| Platinum | 15 m / 150 | 50 | 1000 | 125 | |
8k cP
| 1.02 |
| Legacy material used for adhering solvent cells to composite substrates. |
|
EPM-2423-2
| | 30 M / 150 | 50 | 950 | 150 | |
8.5k cP
| |
| An embedding or potting compound for environmental protection of electronic
assemblies and components |
|
EPM-2461
| Platinum | 24 H / R.T. | 30 | 550 | 400 | 30 |
A:1250k/B:100k cP
| |
| Two-part, static dissipative silicone |
|
EPM-2462
| Platinum | 30 M / 150 | 80 | 500 | | |
| 3.36 |
| Modulus 1400 psi (9.7 Mpa) |
|
EPM-2463
| Tin Condensation | 7 D / R.T. | 80 | 300 | 75 | 55 |
4
| 3.4 |
| Remains Conductive at High Temperature, 0.002 ohm-cm, 1.5 W/mK |
|
EPM-2480
| Platinum | 30 M / 150 | | | | |
2.5k cP
| |
| Two-part, clear silicone gel. For applications requiring low volatility. |
|
EPM-2481
| Platinum | 30 M / 150 | | | | |
A:16k/B:8.5k cP
| |
| Penetration 4 mm, 1.40 Refractive Index |
|
EPM-2482
| Platinum | 40 M / 150 | | | | |
1.8k cP
| |
| Low/High Temperature, Penetration 2 - 4 mm, 1.43 Refractive Index |
|
EPM-2490
| Platinum | 7 D / RTV | 75 | 190 | 30 | 45 |
300k cP
| 1.53 |
| Bulk Thermal Conductivity 1.25 W/mK |
|
EPM-2491
| | 4 h / 65 | 75 | 250 | 55 | 55 |
900k cP
| 1.45 |
| Low outgas, thermally conductive |
|
EPM-2492
| Platinum | 30 m / 150 | 75 | 275 | 40 | |
300k cP
| |
| Two-part, white, thermal interface silicone system, 0.62 W/mK |
|
EPM-2495
| | 30 m / 150 | 55 | 400 | 225 | 55 |
| |
| 0.64 W/(mK) |
|
CV-2500
| Platinum | 15 m / 150 | 50 | 1000 | 125 | |
8k
| 1.02 |
| Pourable, Primed Lap Shear 400 psi (2.8 Mpa) |
|
CV10-2500
| Platinum | 15 m / 150 | 50 | 1000 | 130 | |
7.5k cP
| 1.02 |
| 1:1 Mix Ratio |
|
CV14-2500
| Platinum | 60 m / 65 | 30 | 425 | 150 | |
2.6k cP
| 1.01 |
| Primerless Adhesion |
|
CV15-2500
| Platinum | 15 m / 150 | 50 | 850 | 90 | |
A:3.8k/B:2.7k cP
| 1.02 |
| Primed Lap Shear 225 psi (1.6 Mpa) |
|
CV16-2500
| Platinum | 4 h / 65 | 40 | 650 | 100 | |
3.6k cP
| 1.04 |
| Low/high Temperature, Primed Lap Shear 200 psi (1.4 Mpa) |
|
CV3-2500
| Platinum | 30 m / 150 | | 950 | 100 | |
3k cP
| 1.02 |
| Low Viscosity |
|
CV4-2500
| Platinum | 60 m / 65 | 25 | | | |
1.5k cP
| |
| Low Durometer |
|
CV-2500-2
| Platinum | 30 m / 150 | 50 | 950 | 150 | |
8.5k cP
| 1.05 |
| Low Viscosity, Fast Cure Elastomer, Black |
|
CV-2502
| Platinum | 7 d / R.T., H | 40 | 800 | 200 | |
| 1.06 |
| Low Flow |
|
CV4-2502
| Platinum | 7 d / R.T., H | 45 | 800 | 225 | |
Thixotropic
| 1.06 |
| UV Tracer |
|
CV-2510
| Tin Condensation | 7 d / R.T., H | 45 | 600 | 200 | |
45k cP
| 1.19 |
| Low/High Temperature, Flowable Elastomer |
|
R-2550
| Tin Condensation | 7 D / R.T. | 35 | 500 | 175 | 20 |
9k cP
| 1.08 |
| RTV, Low Viscosity Elastomer |
|
R-2560
| Tin | 7 d / R.T., h | 55 | 700 | 125 | |
31k
| 1.41 |
| For thermal insulating as a firewall sealant or as an ablative coating |
|
R7-2560
| | 7 d / R.T., | 50 | 375 | 110 | 35 |
150k cP
| |
| RTV High Temperature Adhesive/Sealant Silicone Elastomer
NGC Specification QFM-486 |
|
R8-2560
| | 7 d / R.T., H | 45 | 350 | 95 | 45 |
110k cP
| 1.23 |
| RTV High Temperature Adhesive/Sealant Silicone Elastomer
NGC Specification QFM-486 |
|
CV-2566
| Tin Condensation | 7 D / R.T | 55 | 950 | 150 | 40 |
56.8k cP
| 1.49 |
| Pourable, RTV Cure, Primed Lap Shear 575 psi (4.0 Mpa)
NGC Specification C104689 |
|
CV-2566
| Tin Condensation | 7 d / R.T., H | 55 | 950 | 150 | 40 |
55k cP
| 1.49 |
| Pourable, RTV Cure, Primed Lap Shear 575 psi (4.0 Mpa) |
|
CV1-2566
| Tin Condensation | 7 d / R.T., H | 50 | 900 | 160 | |
45k cP
| 1.45 |
| Lower Viscosity, Primed Lap Shear 650 psi (4.5 Mpa) |
|
CV2-2566
| Tin Condensation | 7 d / R.T., H | 55 | 900 | 140 | 40 |
| 1.50 |
| Thixotropic, RTV Cure, Primed Lap Shear 625 psi (4.3 Mpa) |
|
CV-2567
| Tin | 7 d / R.T., H | 21 | 80 | 150 | |
5k
| 1.01 |
| Diluent for Tin Condensation CV Silicones |
|
CV-2568
| Tin Condensation | 7 d / R.T., H | 50 | 175 | 60 | |
125k cP
| 0.64 |
| Long Worktime, Low Density, Primed Lap Shear 100 psi (0.69 Mpa) |
|
CV10-2568
| Platinum | 30 m / 150 | 40 | 235 | 170 | |
A:125k/B:80k cP
| 0.76 |
| Fast Cure, Low Density, Primed Lap Shear 175 psi (1.2 Mpa) |
|
SCV-2585
| Platinum | 15 m / 150 | 35 | 700 | 300 | |
A:56k/B:43k cP
| |
| Pourable Elastomer, Primed Lap Shear 475 psi (3.3) |
|
SCV-2586
| Platinum | 30 m / 150 | 45 | 225 | 150 | |
A:375k/B:275k
| 0.74 |
| Fast Cure, Low Density, Primed Lap Shear 175 psi (1.2 MPa) |
|
R-2588
| | 7 D / R.T., H. | 65 | 750 | 95 | |
825k
| 1.44 |
| Broad temperature range, lap shear 675 psi |
|
SCV-2590
| Platinum | 15 M / 150 | 45 | 950 | 125 | |
8k
| 1.02 |
| Pourable, primed lap shear 375 psi (2.6 MPa) |
|
SCV1-2590
| Platinum | 15 M / 150 | 50 | 925 | 90 | |
A:3.8k/B:2.8k cP
| 1.02 |
| Primed Lap Shear 175 psi (1.2 Mpa) |
|
SCV2-2590
| Platinum | 4 H / 65 | 45 | 475 | 85 | |
3.5k cP
| 1.04 |
| Low / High Temperature, Primed Lap Shear 250 psi (1.7 Mpa) |
|
SCV-2590-2
| Platinum | 15 M / 150 | 50 | 950 | 150 | |
9.5k cP
| 1.06 |
| Low Viscosity, Fast Cure |
|
SCV-2596
| Platinum | 30 M / 150 | 75 | 475 | 90 | |
| 1.19 |
| Electrically Conductive, 2.5 ohm·cm, Carbon Fiber Filled |
|
SCV1-2596
| Platinum | 30 M / 150 | 85 | 450 | | |
| 3.42 |
|